Full text (ru) Assessment of WWER-type reactor vessels radiation lifetime of Ukrainian NPPS
E. U. Grynik, L. I. Chyrko, V. M. Revka
Institute for Nuclear Research, National Academy of Sciences of Ukraine, Kyiv, Ukraine
Abstract: The Ni content in the welds of 9 energetic units of WWER-1000 type NPPs operating in Ukraine now exceeds the standard value. The increase of the Nickel concentration beyond the regulated one is known to lead to the increase of the irradiation embrittlement rate. The highest content of Nickel is in the weld metal of Khmelnitsky NPP-1 and it is equal to 1.88%. Therefore, the paper considers just this case as the most complicated. In the paper the performed analysis of the dependence of the brittle critical temperature of the weld metal on the accumulated neutron fluence has shown the critical temperature not to exceed (with the confidence probability 95%) the regulated dependence. Thus, the state of the weld metal does not limit the design lifetime of the given reactor vessel.
References:1. ПНАЭ Г-7-002-86 "Нормы расчета на прочность оборудования и трубопроводов атомных энергетических установок" (Москва: Энергоатомиздат, 1989) 524 с.
2. Техническое решение о внесении изменений в порядок контроля свойств металла корпусов реакторов ВВЭР-1000 по образцам-свидетелям. ГАН РФ. Инв. №62 1668 (Москва, 1993) 5 с.
3. Принципиальные положения контроля свойств металла КР ВВЭР-1000 по образцам-свидетелям. ГАН РФ. Инв. №60/80. (Москва, 1993) 30 с.
4. Образцы-свидетели. 1152.75.00.000 Формуляр ХАЭС-1, ПО "Атоммаш" (1985) 215 с.
5. Николаев А. В., Николаев Ю. А., Кеворкян Ю. Р. Радиационное охрупчивание материалов корпусов реакторов ВВЭР-1000. Атомная энергия 90 (2001) 359.
6. Морозов А. М., Николаев В. А., Юрченко Е. В. Влияние никеля на радиационное охрупчивание основного металла и металла швов стали 15Х2НМФА-А. Proc. of the 6-th Intern. Conf. on "Materials Issues in Design, Manufacturing and Operation of NPPs Equipment" (St. Petersburg, 19 - 23 June 2000) Vol. 2, p. 372.
7. Определение радиационной нагрузки КР блока №1 ХАЭС в течение 12 и 13 топливных кампаний. 14 топливная кампания: (Отчет по доп. соглашению №1 к рамочному договору №Х/105У "Мониторирование радиационной нагрузки КР ХАЭС-1"). ИЯИ НАН Украины (Київ, 2003) 51 с.
8. Banyuk G. F., Dragunov Yu. G., Piminov V. A., Ryjov S. B. Ageing Degradation & Mitigation. Workshop on Integration Opportunities (Netherlands, Petten, 10-11 Dec. 2001) 6 р.
9. Piminov V., Akbashev I., Maksimov Y. Results of Application of New Russian Regulatory Methodology MPK-CXP-2000 for Integrity Assessment of WWER Reactor Pressure Vessels. Regional Workshop on Structural Integrity Assessment (Germany, Erlangen, 10-14 Dec. 2001) 35 p.
10. Методика определения ресурса корпусов атомных реакторов в процессе эксплуатации. МРК - СХР - 2000. Концерн "Росэнергоатом" (С.-Петербург - Москва, 2000) 47 с.
11. Определение суммарного флюенса быстрых нейтронов на КР блока №1 ХАЭС за первые 12 топливных кампаний: (Отчет по этапу II НИР). ИЯИ НАН Украины (Київ, 2003) 174 с.